Making Strong Parts

Post by Theycallmejohn » Thu Jun 05, 2014 5:35 pm

Guys what are you recommendation on making prints as strong as possible. I wont to build a swiveling arm wall bracket for my monitors but don't want them to split and fall to pieces. Monitor Breaking = bad times.

I know infill can be adjusted but what other recommendation do you guys have. Currently using Lulzbot green but I am still getting some splitting of long parts and breaking off of small parts.

Should I use ABS? Should I use PLA? What else can I do to make them stronger?

Thinking about making something like the links below:

http://www.thingiverse.com/thing:22934
or
http://www.thingiverse.com/thing:216329

User avatar
gannon
Posts: 47
Joined: Wed Jul 10, 2013 11:42 am

Re: Making Strong Parts

Post by gannon » Fri Jun 06, 2014 7:48 am

One immediate thought is to rotate the part when printing so that the layers are set down orthogonal to the force you expect the print to be put under.
Or, print in PLA and do some lost casting. I doubt aluminum will break easily ;)

bam
Posts: 117
Joined: Thu Sep 19, 2013 11:37 pm

Re: Making Strong Parts

Post by bam » Fri Jun 06, 2014 1:00 pm

Theycallmejohn wrote:Guys what are you recommendation on making prints as strong as possible. I wont to build a swiveling arm wall bracket for my monitors but don't want them to split and fall to pieces. Monitor Breaking = bad times.

I know infill can be adjusted but what other recommendation do you guys have. Currently using Lulzbot green but I am still getting some splitting of long parts and breaking off of small parts.

Should I use ABS? Should I use PLA? What else can I do to make them stronger?

Thinking about making something like the links below:

http://www.thingiverse.com/thing:22934
or
http://www.thingiverse.com/thing:216329
I'd recommend ABS and painting the part with acetone. It'll give you an nice finish, but more importantly it'll seal the outer plastic layers together and help prevent splitting. Also, adding more perimeters and solid layers will usually help.

rufu5
Aleph Objects | LulzBot
Posts: 249
Joined: Wed Apr 10, 2013 12:25 am

Re: Making Strong Parts

Post by rufu5 » Fri Jun 06, 2014 3:26 pm

go HAM and print polycarbonate

User avatar
piercet
Posts: 4028
Joined: Sun Aug 25, 2013 1:37 am
Location: Battleground, WA
Contact:

Re: Making Strong Parts

Post by piercet » Sat Jun 07, 2014 1:54 am

In addition to the acetone bath, for parts you relaly need a huge amount of strength around a hole, you can try inserting a large heatset insert, and then drill out the threading to basically make a bushing. They might just sell heat set bushings like that, I haven't looked. but basically the melt insert re-glues all the layers immidiatly surrounding the hole, leading to additional strength right there.

User avatar
Theycallmejohn
Posts: 243
Joined: Sat Dec 28, 2013 6:05 pm
Location: Huntington Beach, CA

Re: Making Strong Parts

Post by Theycallmejohn » Sat Jun 07, 2014 2:15 pm

rufu5 wrote:go HAM and print polycarbonate
What does go HAM mean?

User avatar
piercet
Posts: 4028
Joined: Sun Aug 25, 2013 1:37 am
Location: Battleground, WA
Contact:

Re: Making Strong Parts

Post by piercet » Sun Jun 08, 2014 11:32 am

I'm not sure specifically what HAM refers to, but to print polycarbonate you need a high temperature hot end, like an E3D or similar.

rufu5
Aleph Objects | LulzBot
Posts: 249
Joined: Wed Apr 10, 2013 12:25 am

Re: Making Strong Parts

Post by rufu5 » Mon Jun 09, 2014 7:12 am

Theycallmejohn wrote:
rufu5 wrote:go HAM and print polycarbonate
What does go HAM mean?
http://lmgtfy.com/?q=What+does+go+HAM+mean%3F

User avatar
Theycallmejohn
Posts: 243
Joined: Sat Dec 28, 2013 6:05 pm
Location: Huntington Beach, CA

Re: Making Strong Parts

Post by Theycallmejohn » Mon Jun 09, 2014 1:04 pm

rufu5 wrote:
Theycallmejohn wrote:
rufu5 wrote:go HAM and print polycarbonate
What does go HAM mean?
http://lmgtfy.com/?q=What+does+go+HAM+mean%3F
Some guys like a small ass...

Some guys like a big ass...

But no one likes a smart ass..


So i am guess you a referring to the Go Crazy usage aka the "Hard as a MF". Guess I would need a all metal hotend.

Bam, hows the all metal hotend coming along? Do you need any beta testers?

bam
Posts: 117
Joined: Thu Sep 19, 2013 11:37 pm

Re: Making Strong Parts

Post by bam » Mon Jun 09, 2014 1:49 pm

Theycallmejohn wrote: Bam, hows the all metal hotend coming along? Do you need any beta testers?
Pretty well!

The cast heatsink wound up not being feasible in the quantities we needed, so I'm currently testing out E3D's V6 hotend as well as a custom version of the Hexagon hotend from reprap discount. As soon as we choose which of these nozzles will be on the TAZ mini we'll be releasing a high temp hotend. I'll keep you in mind if we decide to do a beta test phase :)

Cheers